Regularities of glass formation and thermalstability of glassEs in the MF2 – MS – Ga2S3 (M = Mg, Ca, Sr, Ba) systems

Abstract

The glass transition area limits for the samples in the MF2 – MS – Ga2S3 (M = Mg, Ca, Sr, Ba) systems are determined by the experiment. The areas of the glass-forming in ternary systems adjoin to the binary MS— Ga2S3 systems and spread increasing the content of alkaline-earth metalfluoride. The Zachariasen's rule confirms that the increase in the radius of the alkaline-earth metal contained in the glass results in improving the ability of melts to vitrify. The symptomatic temperatures of the glasses formed in the systems are calculated by the differential-thermal analysis.

Экспериментально установлены границы областей стеклования образцов в системах MF2 – MS – Ga2S3 (M = Mg, Ca, Sr, Ba). Области стеклообразования в тройных системах прилегают к двойным системам MS — Ga2S3 и распространяются в сторону увеличения содержания фторида щелочноземельного металла. Увеличение радиуса щелочноземельного металла, входящего в состав стекла, приводит к повышению способности ковалентных расплавов к стеклованию, что подтверждает правило Захариасена. Методом дифференциально-термического анализа определены характеристические температуры стекол, образующихся в системах, и рассчитаны их критерии термической стабильности.