Определение усадки цементного камня в лабораторных условиях

Abstract

The article suggests a method for determining the volume shrinkage of cement slurry. It involves measuring velocity of fluid or gas filtration through a gap between the cement stone and the wall of the device cell formed as a result of volume shrinkage. A standard and widespread cell is used for water loss measurement according to API RP 10B-2. The experiments were carried out with the standard cementing slurries. The shrinkage of heavy cement slurry with the density of 1900 kg/m3 and the shrinkage of light cement slurry with the density of 1600 kg/m3 were determined. The flowrates of nitrogen and kerosene were measured. It is shown that for light cement slurries the suggested method shows good agreement between the experiments and can be applied in practice. For heavy cement slurries the suggested method gives only qualitative results.

В данной статье предложен метод определения объемной усадки цементного раствора, заключающийся в измерении скорости фильтрации жидкости или газа через зазор между цементным камнем и стенкой ячейки прибора, образовавшийся в результате объемной усадки. В методе используется стандартная и широко распространенная ячейка для измерения водоотдачи по стандарту API RP 10B-2. Выполнены эксперименты со стандартными тампонажными системами. Была измерена усадка тяжёлого раствора с плотностью 1900 кг/м3 и облегченного раствора с плотностью 1600 кг/м3. Измерялся расход азота и керосина. В статье показано, что для легкого цемента предложенный метод показывает хорошую сходимость экспериментов и может применяться на практике. Для тяжелых растворов цемента предлагаемый метод дает только качественные результаты.